Filtering material

ABSTRACT

1. A FLUID FILTER WHICH COMPRISES A COMPLEX METALLIC PRODUCT RESULTING FROM REACTING CELLULOSE WITH AN INORGANIC NITRATE OF THE FORMULA ME(NO3)N WHERE ME REPRESENTS A METAL ATOM SELECTED FROM THE GROUP CONSISTING OF MANGANESE, NICKEL, ALUMINUM, CALCIUM, IRON, SODIUM, ZINC, AND COPPER AND N IS A NUMBER CORRESPONDING TO THE VALENCE NUMBER OF THE METAL ATOM.

1974 A. J. HARENDZA-HARINXMA 3,

x-xumnme mm Filed June a, 1973 FIG. 2

United States Patent 3,842,070 FILTERING MATERIAL Alfred Joseph Harendza-Harinxma, Lawrenceville, NJ., assignor to Samuel A. La Paglia, Dean W. Merry, and Peter J. 'Catanese, fractional part interest to each Continuation-in-part of application Ser. No. 210,043, Dec. 20, 1971, which is a continuation of application Ser. No. 69,760, Sept. 4, 1970, both now abandoned. This application June 8, 1973, Ser. No. 368,442

Int. Cl. A24b 15/02; C08b 15/00 US. Cl. 260-212 22 Claims ABSTRACT OF THE DISCLOSURE CROSS-REFERENCE TO RELATED APPLICATION This is a continuation-in-part of my copending application, Ser. No. 210,043 filed Dec. 20, 1971, now abandoned, for Filtering Material, which in turn was a continuation under Rule 60 of my prior application Ser. No. 69,760 filed Sept. 4, 1970 now abandoned, for Filtering Material.

BACKGROUND OF THE INVENTION 1. Field of the Invention Broadly speaking, this invention relates to filtration. More particulary, in a preferred embodiment, this invention relates to the filtration of noxious and offensive gases, particulate material and vapors, from the atmosphere.

2. Description of the Prior Art The rapid increase in the death rate due to lung cancer, emphysema, bronchitis and similar respiratory diseases has been traced to the growing amount of pollution in the air we breath, including the so-called personal air-pollution caused by cigarette smoking. The number of pollutants in the atmosphere are too numerous to list in detail but some of the principal components comprise carbon monoxide and lead from automobile exhausts; sulphur dioxide and soot from the burning of fossil fuel; and, in the case of cigarettes, nicotine, acrolein, phenol, tars, organic acids such as alcohol, acetic acid, ketones, esters, and other hydrocarbons and carbon dioxide, carbon monoxide and oxides of nitrogen.

Medical research has proved beyond doubt that many of the above-described pollutants are carcinogenic and some, such as acrolein (CHyCH-CHO), are ciliastatic, that is to say, they paralyze the cilia which line the trachea and bronchioles. Normally, these whiplike appendages beat to and fro, in rhythmic fashion, and by this action carry foreign bodies up and out of the respiratory tract, thereby preventing foreign particulate matter from accumulating in the respiratory system. When the activity of the cilia is inhibited by acrolein or similar pollutants, harmful particulate material, including in the case of cigarette smoking any tar particles contained in the smoke, easily pass by the paralyzed cilia and collect in the lungs.

In view of the pressing health problem, vast research projects have been conducted, particularly in the cigarette industry, in an attempt to find a filter which will attenuate, or better still, eliminate most of these harmful ele- "ice ments. Unfortunately, the results to date have not been spectacular. While the smoker of a commercially manufactured filter cigarette is undoubtedly better off than if he were smoking a non-filtered cigarette, he nevertheless, runs a significant risk of contracting bronchitis or emphysema or other more dangerous illnesses.

Commercially available cigarette filters typically comprise a solid absorbent, such as activated charcoal or silica gel, sandwiched between a pair of cellulose acetate filter plugs. This type of filter removes from the tobacco smoke a proportion of the liquid or semi-liquid droplets passing through it. This is accomplished by a combination of difiusional, impactive, and direct collision of the droplets with the filter fibers. Upon collision, the droplets are retained on the fibers by the surface attraction between the extremely small particles and the relatively large fiber. Such fibrous filters are, however, not particularly effective for removing vaporized components from the smoke stream by the processes of physical and chemical adsorption. The smooth and non-porous nature of the commonly used fibrous filtering materials, while effective in capturing tobacco smoke droplets, does not present a suflicient surface area to effectively adsorb gaseous molecules. It has been calculated that an ordinary cellulose acetate cigarette filter plug has a surface area ranging from 1,000 to 10,000 square centimeters per gram of material. This aifords insufficient surface area for effective adsorption of gaseous molecules, and has no significant selectivity. In some instances, where a vaporized material is sufficiently soluble in the fibrous material so that its surface concentration is rapidly depleted, a significant removal can be achieved by the process of absorption. An example of such a material present in tobacco smoke is phenol, which has a pronounced solubility in cellulose acetate filtering material. Cellulose acetate filters allow both hydrogen cyanide and hydrogen sulfide to pass through in undesirability high concentration.

In attempts to improve the adsorptive properties of tobacco smoke filters, various treatments of ordinary filtering material and various new fibrous filtering materials have been proposed. Among the materials and treatments proposed, a number of well-known adsorbents such as activated charcoal, alumina, natural and synthetic clays and silica gel have been proposed as additives to tobacco smoke filters. These materials are classified as absorbents and are used in gas-stream treatment because they possess in common the characteristic that their specific surface area exceeds a million square centimeters per gram of material. A good grade of gas adsorbent quality activated carbon, for example, has a specific surface area in excess of 5 million square centimeters per gram. In general, the preferred method heretofore used of including these adsorbents in tobacco filters has been by dusting, spraying, tumbling, slurrying, or otherwise incorporating the finely-divided adsorbent into the fibrous material which forms the filter or a part thereof.

Such adsorbent-containing tobacco smoke filters are only partially effective for several reasons. One is that the adsorbent is often rendered ineffective by the incorporation process and subsequent handling in the cigarette manufacturing and distribution process, in that water, plasticizing agents, glues, adhesives and volatile flavoring materials, in prolonged close contact with the finely-divided adsorbent, partially or completely utilize the adsorbent surface, thus decreasing its capacity to adsorb gaseous molecules from the smoke stream.

Another reason is that when adsorbent and fibrous filtering materials are intimately mixed, condensed droplets tend to be deposited in such a filter on or near an ad sorbent particle, with the result that relatively non-volatile smoke constituents quickly permeate the adsorption and thus reduce its capacity for adsorption of gaseous molecules I Further disadvantages of such known adsorbent filters are that the inclusion of considerable quantities of adsorbent in a tobacco smoke filter has both a marked effect upon the draw resistance of the smoking article, and upon the taste of the smoke stream. A powder of finely divided adsorbent dispersed in a matrix of fibrous filtering elements impedes the flow of smoke through the filter and requires that the smoker apply additional suction to withdraw his normal amount of smoke. If enough adsorbent is included to remove considerable quantities of deleterious materials, the draw resistance is well above a desirable and comfortable level.

On the other hand, segregation of the adsorbent into a portion of the filter separated from the fibrous portion thereof, has pronounced deleterious effects on the taste of the smoke. When adsorbents such as charcoal, alumina, or silica gel are incorporated in a cigarette filter (segregated from the cellulose acetate filter) in sufiicient quantities to considerably reduce the levels of gaseous materials, it is found that the taste of the smoke stream is far from pleasing to experienced smoke tasters. Although some irritating factors are reduced, the smoke is found to have an astringent, bitter, drying taste. Other mineral adsorbents have a similar overall effect, with minor modification in taste and aroma depending on the particular adsorbent. The general result is that a pleasing smoke is obtained only when the amount of adsorbent is reduced to the point where it is well in minor proportion to the fibrous filtering agent. When present at such diminished levels, it is insufficiently effective in removing undesirable smoke constituents.

The problem then is to find a filter which does not rely on adsorption alone for its filtering action but which, nevertheless, is highly efiicient in removing particulate, vapor and gaseous pollutants from the atmosphere. The filter should have application to the control of industrial pollution in general, and to the automobile industry in particular, and should also be of use in the cigarette industry. In this latter regard, the filter should be inexpensive, tasteless and should not add significantly to the amount of draw required from the cigarette.

SUMMARY OF THE INVENTION As a solution to this problem an illustrative embodiment of the invention comprises a fluid filter which comprises cellulose which has been reacted with an inorganic nitrate of the formula Me(NO )n-'H O where Me represents a metal atom selected from the group consisting of Manganese, Nickel, Aluminum, Calcium, Iron, Sodium, Zinc and Copper and n is 1, 2, 3 depending on the valence number of the corresponding metal.

Yet another embodiment of the invention comprises -a method of manufacturing a filter material comprising the steps of forming an aqueous solution of an inorganic nitrate of the formula Me(NO )n-H O where Me represents a metal atom selected from the group consisting of manganese, nickel, aluminum, calcium, iron, sodium, zinc, and copper and n equals 1, 2 and 3, depending on the valence number of the corresponding metal; adding a cellulose-containing material in said aqueous solution; and heating said material to evaporate oil? the aqueous solution remaining and decompose the nitrate.

The invention and its mode of operation will be more fully understood from the following detailed description, taken in conjunction with the drawings, in which:

DESCRIPTION OF THE DRAWINGS FIG. 1 is an isometric, partially cut-away view of an illustrative cigarette utilizing the fluid filter of this invention; and

FIG. 2 is a cross-sectional view of an illustrative to bacco pipe utilizing the fluid filter according to this invention.

DETAILED DESCRIPTION OF THE INVENTION The instant invention arose out of research which was directed towards finding an improved cigarette filter. It was quickly realized, however, that the filter material according to this invention may advantageously be used, by way of example and not of limitation, in the exhaust path of an internal combustion engine; in the flue or smoke-stack of an industrial plant; and at the input or output of an air-conditioning unit, or the like. When so used, the filter is highly efiicient in removing unwanted gaseous and particulate pollutants.

The filter will be described in connection with its use as a cigarette filter; however, its use as a filtering medium for other applications should be borne in mind at all times.

Inorganic nitrates, may bedefined as chemical compounds of the formula Me(NO -mH O, where "Me represents a metal atom and n may be 1, 2, or more, depending on the valence number of the metal. At ordinary temperatures nitrates are crystalline solids or solutions and may be white or colored, depending on the metal constituent. As a group they are the most water soluble of all metal salts and are prepared by reaction of the desired metal, its oxide or its carbonate with nitric acid.

As will be seen from the specific examples to be given below, the filter material according to this invention is prepared by reacting cotton with a metallic nitrate to form a complex organic compound. The reaction is not fully understood.

The resulting complex organic compound may be mixed with other chemical constituents to modify the filtering properties or it may be used alone. Again, the reaction between the filtering material and the pollutants is not fully understood. It is believed to be a true reaction (not merely an adsorption) in which the pollutants are oxidized. This view is strengthened by the results of gas chromatography experiments made on the fluid to be filtered before and after filtration. These experiments indicate an increase in the percentage of oxygen which could not occur in an adsorption process alone.

The inability to properly characterize the filtering material and the manner in which it operates is, of course, no bar to patentability nor to the successful use of the material in filters of various types.

Example I 4.5 grams of cotton was added in mil of a 50 percent by weight manganese nitrate in a porcelain dish and 'heated on a hotplate to a temperature of approximately 250 C. for approximately three hours, or until all the remaining manganese nitrate solution had evaporated, and the remaining nitrate decomposed. During the decomposition of nitrate, N0 gas was observed.

The material remaining was then ground into a fine black powder and mixed with water to form a suspension.

Fresh cotton was then soaked in the suspension and dried to form the filtering material.

Example 11 In the process disclosed in Example I, rather than form a suspension of the black powder in water, the black powder is ground with fresh cotton to impregnate the cotton with the powdered material and form the filter. For use as a cigarette filter, from 60 to 350, preferably mg. of the black powder is ground into about 60 mg. of cotton.

Example III Seventy mil of 50 percent manganese nitrate (MIINO3)Z' solution was mixed with 30 mil of an 85 percent solution by weight of phosphoric acid (H PO Next, 4.5 mg. of cotton was added to the mixture and left to soak for approximately twelve hours, or until the cotton began to decompose.

The resulting gel was placed in a porcelain dish and heated on a hotplate at a temperature of approximately 250 C. until the remaining liquids were evaporated and the nitrate decomposed. A yellowish-brown powder was obtained which may be used as the filtering agent.

Example IV A filter was formed by mixing the following ingredients:

43.4 grams of the black powder of Example I 2.1 grams pure shredded tobacco 34.4 grams of the yellow-brown powder of Example II 1.8 grams charcoal 17.2 grams 120 mesh Pumice 1.1 grams granular thermoplastic powder The charcoal was included to remove any odor which may be added to the taste of the cigarette smoke by the other ingredients. The 120 mesh, partially-ground, pumice is an inert material added to increase the porosity of the filter. The thermoplastic material was obtained for convenience, from commercially available HUNT-brand xerographic toner, but obviously other thermoplastic powders could also be used.

Example V 12 ml. of 50% manganese nitrate (Mn(NO -6H O was mixed with 0.5 g. charcoal and 0.5 g. cotton and left for approximately 12 hours, or until the cotton began to dissolve. Next, the mixture was placed in a porcelain dish and heated on a hotplate at a temperature of approximately 250 C. until all the remaining liquid had been evaporated and the nitrate decomposed.

The material remaining was black in color and when ground yielded a fine black powder, similar to appearance to that obtained in Example I.

Example VI Zinc nitrate (Zn(NO -6H O) was dissolved in dis tilled water to form a 50% solution by weight.

10 ml. of the above solution was mixed with 0.5 grams of cotton and permitted to stand for approximately 12 hours, or until the cotton began to decompose. Next, the mixture was placed in a porcelain dish and heated on a hotplate until the remaining solution was evaporated and nitrate decomposed.

A greyish-white powder was obtained and used as the filter material.

Example VII 125 grams of Aluminum Nitrate (Al(NO -9H O) and 7.5 grams of cotton was dissolved in a mixture of 150 ml. of H and 16 ml. of concentrated nitric acid (HNO 70% strength.

After about 30 minutes, the partially dissolved cotton was removed and placed in a porcelain dish. The dish was then heated on a 250 C. hotplate until the remaining liquid had evaporated and Nitrate decomposed. The resulting solid material was ground to a fine white powder to provide the filter material.

Example VIII The mixture set forth in Example VII was permitted to remain in solution for approximately 90 minutes, or until the cotton had totally dissolved.

The mixture was then evaporated on a hotplate, as in Example VII. During evaporation, N0 gas was observed being driven oif. Again, the residue was ground to a fine white powder.

Example IX Ferric nitrate (Fe(NO -9H O) was dissolved in distilled water to form a 50 percent solution by weight.

Five grams of cotton were then dissolved in 100 mils of concentrated 70 percent nitric acid (HNO Then,

mils of the Fe(NO -9H O solution were mixed with 15 mils of the HNO -cott0n mixture and an additional 1.75 grams of cotton added. The resultant material was per mitted to stand for approximately twelve hours, or until the cotton was completely dissolved. Next, the remaining material was heated on a hotplate at 250 C. until all remaining liquid was evaporated and Nitrate decomposed.

A brownish-yellow powder was obtained which was used as a filter material.

Example X One hundred grams of calcium nitrate (Ca(NO -4H O) was dissolved in mils of H 0.

2.25 grams of cotton was then added to 50 mils of the above solution and 3 mils of concentrated 70 percent nitric acid. The cotton dissolved in the solution.

An additional 2.5 grams of cotton was then added in the solution. Excess HNO and Ca-(NO were then removed by a water rinse.

The cotton was then permitted to dry and after a flash fire burned to dark grey powder which formed the filter material.

Example XI One hundred grams of copper nitrate (Cl1(NO3)2 was dissolved in 100 mils H O. Next, the 1.75 grams of cotton were placed in 20 mils of the above solution and permitted to stand for twelve hours.

The resulting mass was placed in a porcelain dish and heated on a hotplate at 250 C. The mixture burned fiercely leaving a dark brown residue which wasthen ground into a fine powder.

Example XII Ten grams of sodium nitrate (NaNO were dissolved in 20 mils of H 0.

Then 0.25 grams of cotton were dipped in the above solution for 30 minutes and then placed in a crucible and dried.

Next, to remove any excess NaNO remaining, the cotton was subjected to a water rinse and another drying cycle. Finally, approximately three drops of the nitric acid solution described in Example IX was added to the cotton. After approximately 30 minutes, the crucible was placed in a furnace at 400 C. and heated until all remaining liquid had been evaporated and the nitrate decomposed, yielding the filter material which was grayish brown in color.

The filter material which was produced in Examples III, V, VI, VIII, IX, XI, and XII may be mixed with water to form a suspension and cotton, or other similar material, dipped in the suspension to form the actual filter, as described in Examples I and II.

Alternatively, tobacco, charcoal, pumice powder, etc. may be used to dilute the filtering material as described in Example IV.

Actually, the filter material produced according to processes of this invention is so efficient that some cigarette smokers may find its tar and nicotine removing abilities objectionable. In that event, the filter material may be diluted by the addition of more and more inert materials, such as tobacco or pumice. Of course, this increases the amount of harmful material in the smoke.

Unlike conventional adsorption-type filters, which are generally spent after one cigarette, it is an important aspect of this invention that the filter material remains active and may be used for two, three or more cigarettes. It is ideally suited, therefore, for use as a disposable filter element for pipes, cigar holders, cigarette holders, etc.

FIG. 1 illustrates a typical use of the filter material according to this invention.

As shown, cigarette 10 comprises shredded tobacco 11 rolled with a paper cylinder 12. A filter 13 is positioned at an-extreme end of the cigarette and comprises first and second filter retaining means 15 and 16 between which the filter material proper 17 is sandwiched. The filter retaining means may comprise cotton, crepe paper, etc. and the filter material may comprise any of the compositions listed in Examples I through XII.

FIG. 2 ilustrates how the filter may be used in a disposable cartridge for a pipe, or cigarette, or cigar holder.

As shown, pipe 20 comrises a bowl 21 and a stem 22 threadably connected thereto.

A filter cartridge 23 is positioned within the bore of stem 22 and comprises a porous paper cylinder filled with filter material as described in Examples I-XII.

The filter arrangements for use with automobiles, air conditioners, etc. are entirely analogous and are not shown in detail. It will, of course, be necessary to utilize different kinds and quantities of inert filler material, but this is well within the scope of a person skilled in the art.

The sampling and analyses were performed as follow.

The cigarette was inserted into a special Gelman holder, containing a tared Cambridge Filter. The holder was attached to a vacuum system drawing one cc. pull in 2 seconds every minute. Samples of the third and sixth pufi were removed in glass syringes, and injected onto chr0- matographic columns for analysis.

The oxygen, methane-nitric oxide, and carbon monoxide analysis was achieved on a molecular sieve column maintained at C. Separation of other constituents, except carbon dioxide, was achieved on a 12 ft. x A in. Porapak Q Column 2 in. Porapak R Column programmed from 90 C. to 220 C. at 30 C./minute. The carbon dioxide was separated on a 6 ft. x A in. silica gel column maintained at 90 C.

The tar values were obtained by weighing the Cam bridge Filter before and after smoking the cigarette.

Table B, below, gives the result of a chromatographic analysis on the smoke of the same cigarettes tested in Table A.

TABLE B.PEAK HEIGHT (DIVISIONS) Corn- Com- Commercial cigarette A plus- Commerclal mercial mercial cigarette cigarette #1 #2 #4 #4-2 cigarette Retention A no B no short short long long D me Constituents Drag filter filter filter filter filter filter filtered 2.0 Unidentified. 3rd 1, 280 1, 600 815 1, 570 1, 180 1, 200 1, 380 2.0 do- 6th 1, 600 1, 600 1, 170 1, 540 l, 600 1, 600 1, 600 4.4 3rd 140 208 180 156 172 220 4.4 6th 180 252 128 188 212 220 272 5.6 3rd 212 262 144 240 196 192 400 5.6 6th 240 400 160 232 263 256 400 9.5 3rd 176 216 200 164 204 9.5 6th 196 248 144 192 220 220 236 9.. 3rd 144 176 100 160 124 124 164 9.8 6th 156 188 132 168 164 176 192 10. 3rd 48 64 32 48 48 56 44 10. 6th 56 52 32 48 68 54 52 10. 3rd 12 16 4 8 4 8 8 10. 6th 12 20 8 12 12 12 24 11. 3rd 192 100 194 130 162 11. 6th 164 170 104 172 200 200 182 12. 3rd 68 84 48 78 60 72 74 12. 6th 72 90 56 72 82 90 82 13. 3rd 50 56 34 56 40 46 56 13, 6th 50 62 40 50 56 58 42 14. 3rd 16 18 8 18 6 22 10 14. 6th 16 20 10 20 30 24 14 15. 3rd 84 92 52 98 60 104 82 15. 6th 78 94 60 80 110 98 84 3rd 2 2 1 2 1 4 2 8 6th 2 2 1 2 2 4 2 3rd 102 98 74 114 66 110 80 The amount of filtration attainable with the filter material according to this invention is truly spectacular.

Table A, below, lists the results of a laboratory analysis on commercially available cigarettes, both filtered and unfiltered, as well as the same commercially available unfiltered cigarette in combination with several different types of the filter according to this invention.

It will be noted that when applicants filter is used, the tar content drops from a high of 17.9 mg. to a dramatic low of 0.4 mg. Similarly, the oxygen content of the smoke increases from a concentration of 14.0% to 16.0%; carbon dioxide drops from a high of 3.3% to a low of 1.2%; carbon dioxide drops from a high of 5.8% to a low of 4.6% and on subsequent puffs when TABLE 14.-CONCENTRATION PERCENT VOLUME/VOLUME Tars* Methane Carbon Carbon mg./cigand nitric mondici tt arette Puffs Oxygen oxide oxide oxide Commercial cigarette A (no filter) 3- 2 3 0 5 3. 3 5. 8 Do 13. 2 6 12. 0 39 3. 2 9. 7 Commercial cigarette B (no filter) 17. 9 3 14. 0 52 2. 7 8. 3 Dn 17.9 6 12.0 .49 3.2 11.2 Commercial cigarette A (short filter #1) 0. 4 3 16. 0 25 1. 2 4. 6 Dn 0. 4 6 14. 0 38 1. 8 6. 7 Commercial cigarette A (short filter #2)" 3. 5 3 14. 0 52 3. 5 8. 8 o. 3.5 6 14.0 .49 3.4 9.3 Commercial cigarette A (long filter #4) 4. 4 3 14. 0 34 3. 2 8. 6 Do 4.4 6 12.0 .61 5.4 12.3 Commer arette A (long filter #4-2)- 3. 3 3 14. 0 38 2. 5 8. 4 Do 3. 3 6 12. 0 62 3. 8 10. 4 Commercial cigarette D (filtered) 12. 4 3 14. 0 45 2. 6 8. 3 Do 12.4 6 12.0 .57 4.3 10.2

Material collected on 9. Cambridge Filter after 6 pufis (1 pufi, 35 cc. in 2 see.).

"Previously smoked.

the unfiltered cigarette rises to 11.2%, the filter cigarettes according to this invention only rises to 6.7%. Methane and nitric oxide also drop from a high of 0.52% to 0.25%.

Acralein, an important carcinogen, drops from a high of 92 to a low of 52 While hydrogen cynanide drops from a high of 176 to a low of 120. Formaldehyde similarly drops from 14 to 12.

In these analytic tests, the filters used were similar to the manganese nitrate filters described in Examples I through III. Similar, or better, results have been obtained with the filter material described in Examples IV through XII.

The various times, temperatures, concentrations and masses in the Examples are not unduly critical and wide variation is possible. Similarly, the percentages of the various constituents in the filters are not critical and wide variation is again possible.

One skilled in the art may make various changes and substitutions in the processes disclosed, without departing from the spirit and scope of the invention.

What is claimed is:

1. A fluid filter which comprises a complex metallic product resulting from reacting cellulose with an inorganie nitrate of the formula Me(NO )n where Me represents a metal atom selected from the group consisting of manganese, nickel, aluminum, calcium, iron, sodium, zinc, and copper and n is a number corresponding to the valence number of the metal atom.

2. The fluid filter according to claim 1 further including an inert granular material to increase the porosity of the filter.

3. The filter according to claim 2 wherein said inert granular material comprises pumice.

4. The fluid filter according to claim 1 further including activated charcoal to remove any nitrogen-based gases added to the fluid by said inorganic nitrate as it reacts with the fluid to be filtered.

5. The fluid filter according to claim 1 further including a granular thermoplastic powder.

6. A fluid filter which comprises a complex metallic product resulting from reacting cellulose with a mixture of an aqueous solution of manganese nitrate, and phosphoric acid.

7. The fluid filter according to claim 6 further including inert granular material to increase the porosity of the filter.

8. The filter according to claim 7 wherein said inert granular material comprises pumice.

9. The fluid filter according to claim 6 further including activated charcoal to remove any nitrogen-based gases added to the fluid by said manganese nitrate as it reacts with the fluid to be filtered.

10. The fluid filter according to claim 6 further including a granular thermoplastic powder.

11. A fluid-filter which comprises a complex metallic product resulting from reacting cellulose with a mixture of phosphoric acid and an aqueous solution of an inorganic nitrate of the formula Me (NO )n where Me represents a metallic atom selected from the group consisting of manganese, nickel, aluminum, calcium, iron, sodium, zinc and copper and n is a number corresponding to the valence number of the metal atom.

12. The filter according to claim 11 further comprising 3? inert granular material to increase the porosity of the ter.

13. The filter according to claim 12 wherein said inert granular material comprises pumice.

14. The filter according to claim 11 further comprising activated charcoal to remove any nitrogen-based gases added to the fluid by said inorganic nitrate as it reacts With fluid to be filtered.

15. The filter according to claim 11 wherein the inert granular material is a thermoplastic powder.

16. The fluid filter according to claim 11 including a substantially equal proportion by weight of a complex metallic product resulting from reacting cellulose with an aqueous solution of an inorganic nitrate of the formula Me(NO )n where Me represents a metallic atom selected from the group consisting of manganese, nickel, alumi num, calcium, iron, sodium, zinc and copper and n is a number corresponding to the valence number of the metal atom.

17. The filter according to claim 16 further comprising an inert granular material to increase the porosity of the filter.

18. The filter according to claim 16 wherein said inert granular material comprises pumice.

19. The filter according to claim 16 further comprising activated charcoal to remove any nitrogen-based gases added to the fluid by said inorganic nitrate as it reacts with the fluid to be filtered.

20. The filter according to claim 16 further comprising a granular thermoplastic powder.

21. A method of forming a fluid filter material comprising the steps of:

(a) forming an aqueous solution of an inorganic nitrate of the formula Me(NO )n where Me represents a metal atom selected from the group consisting of manganese, nickel, aluminum, calcium, iron, sodium, zinc and copper and n is a number corresponding to the valence number of the metal atom;

(b) mixing said aqueous solution with a solution of phosphoric acid;

(c) adding a cellulose-containing material thereto; and

drying the material of step (c) to drive-'otf excess aqueous solution and phosphoric acid remaining and to decompose the nitrate.

22. The method according to claim 21 including the further step of:

grinding said dried material into a powder.

References Cited UNITED STATES PATENTS 2,423,707 7/1947 Kenyon et al. 260212 2,927,845 3/1960 Plunkett 260220 3,007,917 11/1961 Pauling 260212 3,351,071 11/1967 Belfort 131-264 3,353,543 11/1967 Sproull et al 131-265 3,372,979 3/1968 Reinhardt et a1 260212 3,513,640 5/1970 Moliskey 131-2 7 FOREIGN PATENTS 1,489,730 7/1967 France 131-265 OTHER REFERENCES Industrial and Engineering Chemistry, volume 41, No. 1, January 1949, page 4.

DONALD E. CZAJA, Primary Examiner R. W. GRIFFIN, Assistant Examiner US. Cl. X.R. 

1. A FLUID FILTER WHICH COMPRISES A COMPLEX METALLIC PRODUCT RESULTING FROM REACTING CELLULOSE WITH AN INORGANIC NITRATE OF THE FORMULA ME(NO3)N WHERE ME REPRESENTS A METAL ATOM SELECTED FROM THE GROUP CONSISTING OF MANGANESE, NICKEL, ALUMINUM, CALCIUM, IRON, SODIUM, ZINC, AND COPPER AND N IS A NUMBER CORRESPONDING TO THE VALENCE NUMBER OF THE METAL ATOM. 